Application:
A gasket material for demanding applications that require excellent sealability, conformity to flange surfaces and recovery. The material is designed to swell when in contact with oils and fuels which helps increase the gasket stress for applications that require increased gasket loading that may be previously limited due to insufficient bolting or flange constraints. Applications include water, fuel, oils, coolants and heavy duty equipment applications such as oil pan covers, gear case and flywheel housings.
Composition:
DURLON® 7760 contains high-strength synthetic fibres bonded with high-grade nitrile (NBR) rubber.
Anti-stick properties:
Much effort has gone into improving the anti-stick release agents of all compressed DURLON® products. All DURLON® compressed gasket materials have passed the MIL-G-24696B Navy Adhesion Test (366°F/48 hrs).
Typical Physical Properties:
| Colour
|
Off-White |
| Fibre System | Aramid-Inorganic |
| Binder | Proprietary Blend SBR |
| Temperature Min Max Max, continuous |
-73°C (-100°F) 344°C (650°F) 205°C (400°F) |
| Pressure, Max, bar (psi) Continuous, bar (psi) |
69 (1,000) 34.5 (500) |
| Density, g/cc (lbs/ft3) ASTM F1315 |
1.65 (103) |
| Compressibility, % ASTM F36 |
7-17 |
| Recovery, % ASTM F36 |
50 |
| Creep Relaxation, % ASTM F38 |
<30 |
| Tensile Strength across grain ASTM F152, MPa (psi) |
14.8 (2,100) |
| Fluid Resistance, ASTM F 146, IRM 903 Oil 5 hours at 149°C (300°F) Thickness Increase, % Weight Increase, % ASTM Fuel B 5 hours at 21°C (70°F) Thickness Increase, % Weight Increase, % |
<75
15-30 <30 |
| Sealability , cc/min ASTM 2378 (Nitrogen) |
0.01 |
| Gasket Factors m Y, psi (MPa) Gb, psi (MPa) a Gs, psi (MPa) |
1/16” 6.9 2,412 (16.6) 95 (0.655) 0.609 4 (0.027) |
| Flexibility, ASTM F147 |
4x |